搜索
乌克兰国有企业中央设计机械局“顿涅茨”公司CompanyName:StateEnterpriseCentralDesignMachineryBureauDonetsStreetAddress:145g,ZveinekaCity:LuganskProvince/State:LuganskayaoblastCountry/Region:UkraineZip:91033Telephone:380-642-719599Fax:380-642-719599Omega-300CrystalGrowingFurnaceOmega-300ismainlyusedfortheproductionlargedimensionofsinglecrystalofsapphirebytheKyropoulosmethod.1.Omega-300ishighlyautomatizedmachine.2.Itconsistsoffivemainparts:furnace,heatingpowersystem,high-vacuumsystem,water-coolingsystem,computercontrolsystem3.Heatingpowersystemandpullingmechanismarehighlystableandprecise.4.Heatingpowersystem,pullermechanism,vacuum,water-coolingflowareautomaticallycontrolledbyindustrialcomputer.5.Weightandincrementoftheweightofthegrowingcrystalareobservedonthemonitor.Maximumdiameterofthecrystal300mmMethodofheatingresistiveMaximumheatingtemperature2100°CWorkingpressureinthechamber5x10-5HgmmMaximumchargeamount85kgThecycleofgrowing360hrElectricalrequirements:-voltage3x(380±38)+N-frequency50±0,5HzPowerconsumption,nomore150kVACoolingwaterpressure0,25MPaCoolingwaterconsumption,nomore7m3/hrWeight,nomore2700kgOmega-200CrystalGrowingFurnaceOmega-200ismainlyusedfortheproductionofsinglecrystalofsapphirebytheKyropoulosmethod.1.Omega-200ishighlyautomatizedmachine.2.Itconsistsoffivemainparts:furnace,heatingpowersystem,high-vacuumsystem,water-coolingsystem,computercontrolsystem3.Heatingpowersystemandpullingmechanismarehighlystableandprecise.4.Heatingpowersystem,pullermechanism,vacuum,water-coolingflowareautomaticallycontrolledbyindustrialcomputer.5.Weightandincrementoftheweightofthegrowingcrystalareobservedonthemonitor.Maximumdiameterofthecrystal200mmMethodofheatingresistiveMaximumheatingtemperature2100°CWorkingpressureinthechamber5x10-5HgmmMaximumchargeamount35kgThecycleofgrowing200hrElectricalrequirements:-voltage3x(380±38)+N-frequency50±0,5HzPowerconsumption,nomore90kVACoolingwaterpressure0,25MPaCoolingwaterconsumption,nomore5m3/hrWeight,nomore2100kgSpectr-DCrystalGrowingFurnaceDetailedProductDescriptionSpectr-Dishigh-vacuummachinemainlyusedfortheproductionofmonocrystallinesapphireprofilesbyStepanov(EFG)method.1.Spectr-Dishighlyautomatizedmachine.2.Itconsistsoffiveparts:furnace,heatingpowersystem,computercontrolsystemwithvideocontrolsystem,highvacuum-argonsystem,water-coolingsystem.3.Heatingpowersystemandpullingmechanismarehighlystableandprecise.4.Heatingpowersystem,pullermechanism,vacuum,argonpressureandwater-coolingflowareautomaticallycontrolledbyindustrialcomputer.5.Seedingandcrystalgrowingareobservedthroughthevideosystem.TECHNICALSPECIFICATION1.Heatingmethod:resistive2.Innerchamberdimensions,mm:-diameter:560-height:12503.Maximumworkingareatemperature,oC:21004.Workingenvironmentinchamber1)Vacuum,Pa(mmofmercurycolumn),upto:6.65*10-3(5*10-5)2)Inertargonatexcessivepressureupto,kPa(kgf/cm2):29,4(0,3)5.Upperrodtravelingmechanismparameters:-rodworkingstroke,mm:600-rodmovementworkingspeedrange,mm/h:5-300-marchspeed(acceleratedmotion),mm/min,upto:150-workingandmarchspeedadjustment:smooth,stepless6.Lowerrodtravelingmechanismparameters:-rodstroke,mm:200-rodworkingspeedrange,mm/h:5-300-providedpossibilityofthemovingtherodontheworkingstrokevalue:manually7.Presenceofvideocontrolsystemwithmagnificationdegreewithin:5-78.Externaldimensionsofcrucible:-diameter,mm:140-height,mm:1059.Weightofcharge,kg,nomore:210.PowersupplyiscarriedoutfromthepowersystembyelectricpowerTN-S:threephasefive-wiresystem(withzeroprotectivePEandzeroworkingNwires)ACsupplywithsolidlyearthedneutralofvoltage(400±24)Vandfrequency(50±0,5)Hz.11.Consumedinstallationpowerattemperatureintheworkingarea2100oC,kVA,nomore:5012.Consumptionofcoolingwaterwithtemperature20±5oCandpressure3kgf/cm2,whichisnecessaryforcoolingofthemachine,m3/h,nomore:513.Weight,kg,nomore:2980Spectr-DMCrystalGrowingFurnaceDetailedProductDescriptionSpectr-DMismainlyusedfortheproductionofmonocrystallinesapphireprofilesbyStepanov(EFG)method.采用导模法(EFGmethod)生长蓝宝石单晶型材的高真空晶体生长炉1.Spectr-DMishighlyautomatizedmachine.高度自动化2.Itconsistsoffiveparts:furnace,heatingpowersystem,computercontrolsystemwithvideocontrolsystem,vacuum-argonsystem,water-coolingsystem.由五个部分组成：炉体，加热系统，可视化程序控制系统，真空系统，水冷系统3.Heatingpowersystemandpullingmechanismarehighlystableandprecise.4.Heatingpowersystem,pullermechanism,vacuum,argonpressureandwater-coolingflowareautomaticallycontrolledbyindustrialcomputer.5.Seedingandcrystalgrowingareobservedthroughthevideosystem.TECHNICALSPECIFICATION1.Heatingmethod:resistive加热方式：电阻式2.Innerchamberdimensions,mm:-diameter:560-height:1250炉室空间尺寸3.Maximumworkingareatemperature,oC:21004.Workingenvironmentinchamber1)Vacuum,Pa(mmofmercurycolumn),upto:6,65(0.05)2)Inertargonatexcessivepressureupto,kPa(kgf/cm2):29,4(0,3)5.Upperrodtravelingmechanismparameters:-rodworkingstroke,mm:600-rodmovementworkingspeedrange,mm/h:5-300-marchspeed(acceleratedmotion),mm/min,upto:150-workingandmarchspeedadjustment:smooth,stepless6.Lowerrodtravelingmechanismparameters:-rodstroke,mm:200-rodworkingspeedrange,mm/h:5-300-providedpossibilityofthemovingtherodonthewo