搜索
ICS91.100.10Q11中华人民共和国国家标准GB/T17671一1999idtISO679：1989水泥胶砂强度检验方法（ISO法）Methodoftestingcements-Determinationofstrength1999-02-08发布1999-05-01实施国家质量技术监督局发布GBGB/T17671-1999目次前言··········································································（1)ISO前言······································································（2）1范围········································································（2)2引用标准····································································(2)3方法概要····································································(2)4试验室和设备································································（2)5胶砂组成····································································（7)6胶砂的制备·································································(8)7试件的制备·································································(8)8试件的养护··································································（9）9试验程序····································································（10)10水泥的合格检验····························································(10)11中国ISO标准砂和振实台代用设备的验收检验··································(11)GB/T17671一1999前言本标准是根据ISO679：1989（水泥试验方法一强度测定）制定的，主要内容与ISO679完全一致，某些地方根据中国情况作了修订。其抗压强度检验结果与ISO679：1989等同。本标准采用中国产的ISO标准砂；其鉴定、质量验证与质量控制以德国标准砂公司的ISO基准砂为基准材料。本标准规定可用全波振幅0.75nnn，频率1800-3000次/min的振动台为代用振实设备，其振实操作细则列人第7章中。本标准测定结果有异议时以基准法为准。本标准在以下三个方面较ISO679：1989作了更具体的规定：1．在1范围”中增加“本标准适用于硅酸盐水泥、普通硅酸盐水泥、矿渣硅酸盐水泥、粉煤灰硅酸盐水泥、复合硅酸盐水泥、石灰石硅酸盐水泥的抗折与抗压强度的检验。其他水泥采用本标准时必须研究本标准规定的适用性”。2.在“8.1脱模前的处理和养护”中增加“两个龄期以上的试体，在编号时应将同一试模中的三条试体分在两个以上龄期内”。3.在“10.2试验结果的确定”中增加“10.2.1抗折强度，以一组三个棱柱体抗折结果的平均值作为试验结果。当三个强度值中有超出平均值士10％时，应剔除后再取平均值作为抗折强度试验结果”。本标准由国家建筑材料工业局提出。本标准由全国水泥标准化技术委员会归口。本标准由中国建筑材料科学研究院水泥科学与新型建筑材料研究所负责起草。本标准主要起草人：张大同、王文义、白显明、杨基典、肖忠明、颜碧兰、王听、陈萍、刁志坚、江丽珍、赵双全。GB/T17671一1999ISO前言ISO（国际标准化组织）是世界性国家标准部门（ISO成员单位）的联合会。国际标准起草工作通常是由ISO技术委员会完成的。对技术委员会已确定课题感兴趣的每一个成员单位有权向委员会提出建议，与ISO联络的政府和非政府国际组织也可参加工作。对于所有电工材料标准化工作ISO和国际电工委员会（IEC）进行共同研究。由技术委员会起草的国际标准草案在ISO接受为国际标准之前应得到其成员的认可。按ISO程序要求至少有75%的成员单位表示同意。国际标准ISO679是由ISO/TC74水泥和石灰技术委员会起草的。中华人民共和国国家标准水泥胶砂强度检验方法（ISO法）GB/T17671一1999Methodoftestingcements一DeterminationofstrengthideISO：19891范围本标准规定了水泥胶砂强度检验基准方法的仪器、材料、胶砂组成、试验条件、操作步骤和结果计算等。其抗压强度测定结果与ISO679结果等同。同时也列人可代用的标准砂和振实台，当代用后结果有异议时以基准方法为准。本标准适用于硅酸盐水泥、普通硅酸盐水泥、矿渣硅酸盐水泥、粉煤灰硅酸盐水泥、复合硅酸盐水泥、石灰石硅酸盐水泥的抗折与抗压强度的检验。其他水泥采用本标准时必须研究本标准规定的适用性。2引用标准下列标准所包含的条文，通过在本标准中引用而构成为本标准的条文。本标准出版时，所示版本均为有效。所有标准都会被修订，使用本标准的各方应探讨使用下列标准昀新版本的可能性。GB/I6003-1985试验筛JC/T681-1997行星式水泥胶砂搅拌机JC/T682-1997水泥胶砂试体成型振实台JC/T683-199740mm×40mm水泥抗压夹具JC/T723-1982(1996）水泥物理检验仪器胶砂振动台JC/T724-1982(1996）水泥物理检验仪器电动抗折试验机JC/T726-1997水泥胶砂试模3方法概要本方法为40mm×40mm×160mm棱柱试体的水泥抗压强度和抗折强度测定。试体是由按质量计的一份水泥、三份中国ISO标准砂，用0.5的水灰比拌制的一组塑性胶砂制成。中国ISO标准砂的水泥抗压强度结果必须与ISO基准砂的相一致（见第11章）。胶砂用行星搅拌机搅拌，在振实台上成型。也可使用频率2800-3000次/min，振幅0.75mm振动台成型（见第11章）。试体连模一起在湿气中养护24h，然后脱模在水中养护至强度试验。到试验龄期时将试体从水中取出，先进行抗折强度试验，折断后每截再进行抗压强度试验。4试验室和设备4.1试验室试体成型试验室的温度应保持在20℃土2℃，相对湿度应不低于50%。试体带模养护的养护箱或雾室温度保持在20℃±1℃，相对湿度不低于90%。试体养护池水温度应在20℃±1℃范围内。试验室空气温度和相对湿度及养护池水温在工作期间每天至少记录一次。、养护箱或雾室的温度与相对湿度至少每4h记录一次，在自动控制的情况下记录次数可以酌减至一天记录二次。在温度给定范围内，控制所设定的温度应为此范围中值。4．2设备4．2．1总则设备中规定的公差，试验时对设备的正确操作很重要。当定期控制检测发现公差不符时，该设备应替换，或及时进行调整和修理。控制检测记录应予保存。对新设备的接收检测应包括本标准规定的质量、体积和尺寸范围，对于公差规定的临界尺寸要特别注意。有的设备材质会影响试验结果，这些材质也必须符合要求。4．2．2试验筛金属丝网试验筛应符合GB/T6003要求；其筛网孔尺寸如表1(R20系列）。表1试验筛系列网眼尺寸mmR202.01.61.00.500.160.0804．2．3搅拌机搅拌机（见图1)属行星式，应符合JC/T681要求。用多台搅拌机工作时，搅拌锅和搅拌叶片应保持配对使用。叶片与锅之间的间隙，是指叶片与锅壁昀近的距离，应每月检查一次。4．2．4试模试模由三个水平的模槽组成（见图2），可同时成型三条截面为40mmx40mm，长160mm的棱形试体，其材质和制造尺寸应符合JC/T726要求。当试模的任何一个公差超过规定的要求时，就应更换。在组装备用的干净模型时，应用黄干油等密封材料涂覆模型的外接缝。试模的内表面应涂上一薄层模型油或机油。成型操作时，应在试模上面加有一个壁高20mm的金属模套，当从上往下看时，模套壁与模型内壁应该重叠，超出内壁不应大于lmm。为了控制料层厚度和刮平胶砂，应备有图3所示的二个播料器和一金属刮平直尺。4.2.5振实台振实台（见图4）应符合JC/T682要求。振实台应安装在高度约400mm的混凝土基座上。混凝土体积约为0.25时，重约600kg。需防外部振动影响振实效果时，可在整个混凝土基座下放一层厚约5mm天然橡胶弹性衬垫。将仪器用地脚螺丝固定在基座上，安装后设备成水平状态，仪器底座与基座之间要铺一层砂浆以保证它们的完全接触。注：振实台的代用设备振动台见11.74.2.6抗折强度试验机抗折强度试验机应符合1C/T724的要求。试件在夹具中受力状态如图5。通过三根圆柱轴的三个竖向平面应该平行，并在试验时继续保持平行和等距离垂直试体的方向，其中一根支撑圆柱和加荷圆柱能轻微地倾斜使圆柱与试体完全接触，以便荷载沿试体宽度方向均匀分布，同时不产生任何扭转应力。抗折强度也可用抗压强度试验机（见4.2.7)来测定，此时应使用符合上述规定的夹具。4．2．7抗压强度试验机抗压强度试验机，在较大的五分之四量程范围内使用时记录的荷载应有士196精度，并具有按2400N/s±200N/s速率的加荷能力，应有一个能指示试件破坏时荷载并把它保持到试验机卸荷以后的指示器，可以用表盘里的峰值指针或显示器来达到。人工操纵的试验机应配有一个速度动态装置以便于控制荷载增加。压力机的活塞竖向轴应与压力机的竖向轴重合，在加荷时也不例外，而且活塞作用的合力要通过试件中心。压力机的下压板表面应与该机的轴线垂直并在加荷过程中一直保持不变。压力机上压板球座中心应在该机竖向轴线与上压板下表面相交点上，其公差为±1mm。上压板在与试体接触时能自动调整，但在加荷期间上下压板的位置应固定不变。试验机压板应由维氏硬度不低于HV600硬质钢制成，昀好为碳化钨，厚度不小于l0mm，宽为40mm±0.1mm，长不小于40mm。压板和试件接触的表面平面度公差应为0.Olmm，表面粗糙度(Ra）应在0．1-0．8之间。当试验机没有球座，或球座已不灵活或直径大于120mm时，应采用4.2.8规定的夹具。注1试验机的昀大荷载以200-300kN为佳，可以有二个以上的荷载范围，其中昀低荷载范围的昀高值大致为昀高范围里的昀大值的五分之一。2采用具有加荷速度自动调节方法和具有记录结果装置的压力机是合适的。3可以润滑球座以便使其与试件接触更好，但在加荷期间不致因此而发生压板的位移。在高压下有效的润滑剂不适宜使用，以免导致压板的移动。4“竖向”、“上”、“下”等术语是对传统的试验机而言。此外，轴线不呈竖向的压力机也可以使用，只要按11．7规定和其他要求接受为代用试验方法时。4．2．8抗压强度试验机用夹具当需要使用夹具时，应把它放在压力机的上下压板之间并与压力机处于同一轴线，以便将压力机的荷载传递至胶砂试件表面。夹具应符合JC/T683的要求，受压面积为40mm×40mm。夹具在压力机上位置见图6，夹具要保持清洁，球座应能转动以使其上压板能从一开始就适应试体的形状并在试验中保持不变。使用中夹具应满足JC/T683的全部要求。注1可以润滑夹具的球座，但在加荷期间不会使压板发生位移。不能用高压下有效的润滑剂。2试件破坏后，滑块能自动回复到原来的位置。5胶砂组成5.1砂5.1.1总则各国生产的ISO标准砂都可以用来按本标准测定水泥强度。中国ISO标准砂符合IS