QC控制保温板面层开裂(TUMU)

整理文档很辛苦,赏杯茶钱您下走!

免费阅读已结束,点击下载阅读编辑剩下 ...

阅读已结束,您可以下载文档离线阅读编辑

资源描述

1运用QC方法控制聚苯乙烯外保温板面层厚抹灰开裂小组名称:山西财经大学北校11#高层住宅楼项目部QC小组发布单位:中建土木工程公司发布人:沈拥军23发布程序一、工程概况·································································4二、QC小组概况·····························································5三、选题理由·································································6四、活动目标·································································7五、现状调查与分析·····················································8六、第一次PDCA循环·····················································9七、第二次PDCA循环·····················································14八、效果检查与对比·····················································18九、效益分析·································································19十、施工技术纳入标准化·············································20十一遗留问题及今后打算·············································214一、工程概况山西财经大学北校11#高层住宅楼位于太原市南内环街339号,山西财经大学北校院内,工程总建筑面积52900平方米,地下2层、地上29层(包含2个设备层),为纯剪力墙结构。工程1-3层为商场用房,4-27层为住宅用房,3、4和15、16层之间各有一个设备层。本工程外墙保温均采用50厚双面钢丝网架聚苯乙烯保温板进行外保温,面层为18mm厚水泥砂浆及防水弹性外墙涂料,在水泥砂浆中按水泥重量的1%掺加抗裂剂,阴阳角及保温板接缝处铺设钢丝网片。5二、QC小组概况序号姓名学历职务职称工作内容备注1刘爱军大专组长工程师主持全面工作本课题属于技术攻关型2刘瑞金大专副组长工程师协助组织与实施3王子军大本组员工程师技术指导4张传武高中组员技师质量对比检查5苏日全中专组员技术员安全措施实施6王荣富高中组员技术员技术措施实施7代一大专组员助理工程师两算对比8唐福辉高中组员经济师材料质量控制9朱丛良高中组员班长施工工序控制10郝建华高中组员班长砂浆配比控制山西财经大学11#高层住宅楼项目部QC小组成立于2004年6月5日并开始活动,2004年9月30日活动结束。小组共有10人组成,均受过TQC教育,有着丰富的QC小组活动经验。QC小组人员组成概况如下:6三、选题理由1、因本工程为集资建房,建设单位不增加投资使用聚合物砂浆与网格布。2、太原市类似外保温涂料饰面工程均出现大面积面层开裂。3、单位工程质量要求较高,合同目标为确保“汾水杯”。4、保温板保护层一旦发生开裂,墙体保温性能将发生很大改变,不能满足设计的节能要求,并影响墙体的质量。5、工程位于山西财经大学北校园内,外墙抹灰如出现开裂,将对住户的观感上和心理上造成不良影响,并影响我单位在太原地区的声誉。7四、活动目标1、总结“聚苯乙烯外保温板面层厚抹灰开裂”质量控制方法与措施,并纳入标准化管理;2、确保“聚苯乙烯外保温板面层厚抹灰”质量达到优良标准;3、通过运用该QC方法,为业主(建设单位)节约投资34万元左右。8五、社会调查与分析通过对太原市已完工的类似工程项目进行现场抽样调查,对“聚苯乙烯外保温板面层厚抹灰开裂”的原因分析统计如下:序号调查内容调查数量操作规范项目数量操作规范所占比例1严格控制分层抹灰厚度6个项目1个项目16.7%2养护期间,抹灰层始终保持湿润状态4个项目1个项目20%3砂浆搅拌时间是否延长6个项目3个项目50%4抗裂剂掺加是否专人负责4个项目2个项目50%5钢丝网架是否居凹槽中3个项目1个项目33%6工序操作是否规范4个项目1个项目25%9六、第一次PDCA循环1、现场调查为确保“聚苯乙烯外保温板面层厚抹灰”施工质量,我们利用28层墙体进行模拟施工试验,其结果统计如下:序号项目不合格点频数累计频数累计频率(%)1保温板面层抹灰局部存在0.5mm宽以上的裂纹333373.32保温板接缝处等特殊部位局部出现空鼓现象74088.93局部平整度、阴阳角方正允许偏差过大44497.84外墙四周分格条不能严格控制在一个水平面上,影响观感质量145100102、根据以上调查作排列图如下:局部平整度、阴阳角方正允许偏差过大保温板面层抹灰局部存在0.5mm宽以上的裂纹外墙四周分格条不能严格控制在一个水平面上,影响观感质量保温板接缝处等特殊部位局部出现空鼓现象33404544073.388.997.8100频数N=45累计频率(%)0113、运用因果特性图对现状调查进行分析:机械环境材料方法楼层给水管水压低风力大白天气温偏高加压泵出现故障钢丝网片凸起聚苯板表面光滑、不吸水在0.5mm宽以上的裂纹保温板面层抹灰局部存掺入EC-抗裂剂后,砂浆搅拌不充分124、经以上分析,造成“保温板面层抹灰砂浆局部存在0.5mm宽的裂纹”的主要原因为:(1)聚苯板表面光滑、不吸水;(2)掺入EC-抗裂剂后,砂浆搅拌不充分;(3)加压泵出现故障,造成养护聚苯板表面抹灰砂浆时所需用水供应不及时;(4)钢丝网片凸起。135、针对以上原因,我们编制了相应对策,详见对策表一:对策表一序号主要问题目标措施负责人1保温板表面光滑、不吸水使保温板表面和砂浆之间能牢固的粘结在一起通过掺入EC-砂浆抗裂剂,提高保温板基层与砂浆的粘结强度刘瑞金2掺入EC-抗裂剂后,砂浆搅拌不充分确保掺入EC-抗裂剂与砂浆均匀混合将搅拌时间提高30秒张传武3加压水泵出现故障确保施工时正常供水1、加强机械保养2、增加备用加压水泵苏日全4保温板局部钢丝网片凸起钢丝网片平展、固定牢固1、严格工序交接制度2、加大检查力度王容富141、通过第二次PDCA循环,制定了有针对性的对策并认真实施,基本上消除了“保温板面层抹灰局部存在0.5mm宽以上的裂纹”的质量通病,接着对所有施工部位进行了检查,统计结果如下:序号项目不合格点频数累计频数累计频率(%)1保温板接缝处等特殊部位的面层抹灰出现比较明显的开裂272771.12细部构造观感质量达不到优良标准93694.73局部平整度超过允许偏差238100七、第二次PDCA循环:152、根据上述统计结果,作排列图如下:保温板接缝处等特殊部位的面层抹灰出现比较明显的开裂细部构造观感质量达不到优良标准22793836071.194.7100频数N=38累计频率(%)0局部平整度超过允许偏差163、对“保温板接缝处等特殊部位的面层抹灰出现比较明显的开裂”这一现状进行如下因果分析:方法环境材料工艺保温板面层抹灰养护时间与养护力度均不够昼夜温差达7℃左右分层抹灰厚度偏差未严格执行技术交底特殊部位保温板破损抹灰出现明显开裂特殊部位保温板面层特殊部位的钢丝网片凸起174、经以上因果分析,得出影响“特殊部位保温板面层抹灰明显开裂”的主要原因,并编制了相应对策,详见对策表二。对策表二序号主要问题目标措施负责人1特殊部位的钢丝网片凸起使钢丝网片平展,固定牢固1、严格特殊部位的工序交接制度2、重新修整特殊部位的钢丝网片刘瑞金2保温板面层抹灰养护时间与养护力度均不够通过养护,增强保温板面层抹灰砂浆的粘结强度注重对特殊部位的保温板面层抹灰养护,使之在养护期间始终保持湿润状态王子军3分层抹灰厚度偏差使分层抹灰厚度与总厚度均得到有效控制1、加强中间环节的检查与验收力度2、分层抹灰,分层检查与验收苏日全18八、效果检查与效果对比:1、本QC小组成员,检查最终效果时发现:经过两次PDCA循环,特别是两次PDCA循环过程中均包含的“主要原因分析、对策制定、措施实施”,影响“聚苯乙烯外保温板面层厚抹灰开裂”的主要因素已经得到了有效的控制。2、效果对比:序号主要影响因素不合格点频率(%)活动前活动后1保温板面层抹灰局部存在0.5mm宽以上的裂纹73.332保温板接缝处等特殊部位的面层抹灰出现比较明显的开裂71.103细部构造观感质量达不到优良标准23.604局部平整度、阴阳角方正允许偏差偏大8.9219九、效益分析:1、运用该QC方法改进了施工方案:原方案采用聚合物砂浆及耐碱网格布,需投资18.4元/m2(其中聚合物砂浆16.4元/m2,耐碱网格布2元/m2),改进了施工方案后,仅投资1.18元/m2,该工程外墙抹灰面积共2万m2,共产生经济效益34.44万元。2、取得了良好的社会效益。施工质量受到了监理公司、建设单位的一致好评,太原市的一些地方施工单位纷纷来工地参观并学习如何有效地控制与消除“聚苯乙烯外保温板面层厚抹灰开裂”的质量管理方法与具体控制措施。20十、施工技术纳入标准化:1、完善本课题施工方法,总结控制聚苯乙烯外保温板面层厚抹灰开裂的施工工艺。2、制定控制聚苯乙烯外保温板面层厚抹灰开裂的施工标准,作为今后同类工程施工的参考,施工工艺标准如下:安装50厚双面钢丝网架聚苯乙烯外保温板(此工序随主体砼结构已完成)→冲筋(控制砂浆抹灰层总厚度)→用红色作标记,分别标示出三次分层抹灰厚度→计算好水泥砂浆水灰比→将EC-砂浆抗裂剂按水泥重量1%的比例溶于所需水中→加入水泥搅拌成水泥砂浆→适当延长砂浆搅拌时间→按所标记的厚度分三次成活→分层抹灰,分层养护→加强面层养护21十一、遗留问题及今后打算:1、遗留问题破损保温板部位的修补方法是本课题的薄弱环节,有待进一步技术攻关。2、今后打算认真总结QC小组活动经验,继续开展类似的QC小组活动,本QC小组确定下次活动的课题是“运用QC方法,确保植筋施工质量”。

1 / 21
下载文档,编辑使用

©2015-2020 m.777doc.com 三七文档.

备案号:鲁ICP备2024069028号-1 客服联系 QQ:2149211541

×
保存成功