专业英语(英语科技论文results写法)

Resultsanddiscussion第七小组成员：丁艳然、申妮、刘迪、张益飞、王晓燕、齐园园、于梦妍、石进荣、赵高杰、陈冬、刘文帅主讲人：XXXTableofContentsExample1Introductionofresults2Descriptionofimportantresults3Discussionofresults4Templates5Results一般而言，结果部分的内容包含下列三个主要项目：介绍研究结果，往往以一个句子指出反映完整研究结果的图表。概述最重要的研究结果。对研究结果作出评论或概括由这些结果得到的推论。以上三个项目可能含在几个段落中多次出现。而且每个段落通常由这三个项目组成，段落的第一句为第一个项目，第二个项目是段落的主要部分，第三个项目则是由段落的最后的一、两个句子表达。Example1Theseparatorshouldhaveuniformporesizedistributiontoavoidperformancelosses,whichisduetounevencurrentdensities.Someresearchshowsthatsub-micrometerporedimensionsarecriticalforpreventinginternalshortsbetweentheanodeandthecathodeofthelithium-ioncell,particularlyastheseparatorsareasthinas25mmorless.TheinfluenceofPPTApulpdosagetothemaximumandaverageporesizeofseparatorisshowninFigure3.WiththeincreaseofPPTApulpdosage,themaximumporesizeandaverageporesizeoftheseparatorremainonadownwardtrend.WhenthePPTApulpdosagereaches40%,theporesizeoftheseparatorisdecreasedobviously.Theporesizeoftheseparatorcanbewellcontrolledtolessthan1mm.该隔膜应孔径分布均匀，以避免由于不均匀造成性能损失。研究表明，亚微米孔隙尺寸是针对预防性内部的阳极和锂离子电池的阴极之间的短路的关键，特别是隔膜是薄如25毫米或更小的。PPTA浆液剂量对隔膜最大和平均孔径的影响示于图3。随着PPTA浆液剂量的增加，最大孔径和平均孔径都呈下降的趋势。当PPTA浆液剂量达40％时，隔膜的孔隙尺寸明显减小，隔膜的平均孔隙尺寸可以很好地控制到小于1mm。Figure3.TheinfluenceofPPTApulpdosagetotheporesizeofseparator.图3PPTA剂量对隔膜的孔径的影响Example2TheporesizedistributionoftheseparatorswithPPTApulpdosagerangingfrom20%to100%isshowninFigure4.Itcanbeseenthattheporesizedistributionisnotcontinuous.Partsoflargeporesappearnearthemaximumporesize,andanothercentralizedzoneofscatterisneartheaverageporesize.Thereasonforthediscontinuousdistributionoftheporesizemightbethatthemaximumporesizedependsonthecoarsestfiber'sdiameterandthedefectsofnonwoven,buttheaverageporesizedependsonthemostcommonfiberdiameter.InFigure4a,whenPPTAcontentis20%,therearealmost95%poresintherangeof0.720–10.000mm,butthemaximumporesizeofwet-laidnonwovenis26.923mm.Thismeanstheseparatormayhavesomedefectsuchaspinholesandcannotmeettherequirementoftheseparator.InFigure4f,theporesizedistributionoftheseparatorpreparedwithpurePPTApulpisshown.Thereareabout3%oftheporesnearthemaximumporesizeof0.895mm,andalmost97%oftheporesareattherangeof0.118mm–0.500mm,whichindicatesthattheseparator’suniformityisimprovedobviously.PPTA浆液剂量范围从20％到100％的孔径分布示于图4。该孔径分布是不连续的，孔径分布最多部位附近出现最大孔径。孔径的非连续分布原因可能是最大孔径取决于纤维的最大直径，但其平均孔径依赖于最常见的纤维直径。在图4A中，当PPTA含量为20％，孔隙在0.720μm-10.000μm的范围内的占95％，但此时湿法成网非织造布的最大孔径为26.923μm。这意味着隔膜可能有一些缺陷不能满足隔膜的要求：如针孔。如图4F中，100%纯PPTA量时的孔径分布情况：有97％的小孔分布在0.118μm-0.500μm的范围内，只有3%的小孔分布在最大孔径为0.895μm附近。这表明该分离器的均匀性得到明显改善。Example2Figure4.(a)TheinfluenceofPPTApulpdosagetotheporesizedistributionofseparator(PPTApulpdosageis20%);(b)TheinfluenceofPPTApulpdosagetotheporesizedistributionofseparator(PPTApulpdosageis40%);(c)TheinfluenceofPPTApulpdosagetotheporesizedistributionofseparator(PPTApulpdosageis60%);(d)TheinfluenceofPPTApulpdosagetotheporesizedistributionofseparator(PPTApulpdosageis80%);(e)TheinfluenceofPPTApulpdosagetotheporesizedistributionofseparator(PPTApulpdosageis90%);(f)TheinfluenceofPPTApulpdosagetotheporesizedistributionofseparator(PPTApulpdosageis100%).（A）PPTA浆液用量为20％（B）PPTA浆液用量为40％（C）PPTA浆液用量为60％（D）PPTA浆液用量为80％（E）PPTA浆液用量为90％（F）PPTA浆液剂量为100％Example3FromFigure7,thetearindexincreasesatfirstandthendecreasesasthePETfiberdosageincreases.Thisisbecause,initially,thebinderfibersleadtoanincreaseofthebondingstrengthofthePPTAfibersandwhenthePETfibercontentreachesacertainpoint,thebondingfibersformalowtearstrengthmembraneitself.WhenthePETdosageis20%,thetearindexoftheseparatoris5.16mN·m2·g-1,whichisincreasedby59%thanthatofthepurePPTApulp.Basedontheanalysisoftheporesizeandthemechanicalproperties,thewet-laidnonwovenmaterialwhosePETcontentis20%ischosen,asapreference,forthefollowingpropertiesstudy.从图7中得出，撕裂指数随PET纤维含量增大而增加，到达一定剂量后开始降低。这是因为：开始时粘合纤维与PPTA纤维接合，强度开始增加，但当PET纤维的含量达到某一点时，粘合纤维的撕裂强度低隔膜本身的强度，所以撕裂强度开始下降。当PET用量为20％时，隔板的撕裂指数为5.16mN·m²/g，与纯PPTA浆液相比，增大59%。基于前面对孔径和机械性能等性能的分析，可以得出湿法成网的非织造材料中PET含量为20％时性能较好又能满足作为电池隔膜的要求，因此对20%PET、80%PPTA混合的非织造材料隔膜的性能进行研究。Figure7.TheinfluenceofPETfiberdosagetothetearindexofseparator.图7PET纤维剂量对隔膜撕裂指数的影响Example4InFigure10,theLOIofpolyolefinmembraneandnonwovenmaterialdecreaseswiththeincreaseoftemperature.TheLOIofthenonwovenseparatorishigherthanthatofthepolyolefinmembraneatthesametemperaturebecauseoftheexcellentflameretardancypropertyofPPTAfiber.在图10中，聚烯烃膜和非织造隔膜的LOI指数随温度增加而降低。在相同温度下，由于芳纶纤维的优异的阻燃性特性，无纺布隔板的LOI指数是比聚烯烃膜的高。Figure10.TheLOIofwet-laidnonwovenandpolyolefinmembrane.图10湿法成网非织造布和聚烯烃膜的LOI指数Example5WhenFAMEsynthe-sistestswereperformedwithchangingtheparameterssuchasCaOloadingamount,capsuleloadingamount,methanol/oilmolarratio,reactiontemperature,andstirringrate,theoptimalconditionwasfoundtobe0.08g,0.8g,12,308K,350rpm,respectively.通过改变参数，如氧化钙负载量、胶囊负载量、甲醇/油摩尔浓度、反应温度和搅拌速度，完成了脂肪酸甲酯的合成测试，并得到了最佳的反应条件，分别是氧化钙负载量，0.08g、胶囊负载量，0.8g,甲醇/油摩尔浓度，12,反应温度，308K,搅拌速度350rpm。IntroductionofresultsVerb:–show,present,display,summarize,depict,illustrate（注意：当图表用于作某种总结时，才可使用summarize,而illustrate只有在指图形时才可使用。）Voice:–Active:Diagram/tableassubject（主动：图/表作为主题）–Passive:Resultcontentassubje