高碱铝硅酸盐玻璃的超薄浮法工艺探索-田英良

32　22201011武　汉　理　工　大　学　学　报JOURNALOFWUHANUNIVERSITYOFTECHNOLOGYVol.32　No.22　Nov.2010DOI:10.3963/j.issn.1671-4431.2010.22.027田英良1,梁新辉2,张　磊2,孙诗兵2(1.,430070;2.,100124)　:　高碱铝硅酸盐玻璃具有优良的力学性能,尤其在硬度、韧性和抗划伤等方面表现突出,是电子信息产品的触摸屏幕和手写屏的优选保护材料,依据高碱铝硅酸盐玻璃温度-黏度特性曲线,探索浮法工艺生产超薄高碱铝硅酸盐玻璃的工艺技术要点。:　铝硅酸盐玻璃;　浮法工艺;　超薄:　TQ171:　A:1671-4431(2010)22-0102-04ExplorationofUltrathinHigh-alkaliAlumino-silicateGlassbyFloatProcessTechnologyTIANYing-liang1,LINGXin-hui2,ZHANGLei2,SUNShi-bing2(1.SchoolofMaterialsScienceandEngineering,WuhanUniversityofTechnology,Wuhan430070,China;2.SchoolofMaterialsScienceandEngineering,BeijingUniversityofTechnology,Beijing100124,China)Abstract:　High-alkalialumino-silicateglasseshaveexcellentmechanicalproperties,especiallyinthehardness,toughnessandresistancetoscratch,itisthepreferredprotectivematerialfortouchscreenofelectronicinformationproducts.Inthispa-per,temperature-viscositycurvewasmeasured,thefeasibilityofproducingultrathinglassbyfloatglassprocess.Keywords:　alumino-silicateglass;　floatprocess;　ultrathin:2010-08-15.:(1969-),,,.E-mail:[e-mail],。,,、,(、PDA、MP3、GPS、(UMPC)),,[1]。,、、,iPhoneiPad,20108。,1mm,。[2],,,;,,,TFT-LCD。,,,,。1　1。1　w/%SiO2Al2O3MgONa2OK2O60.017.53.514.53.51.0100.00　　,Al2O3,,、,。,,,。12,2--1。2　lgη/(dPa·S)2.03.04.07.611.513.013.414.5/℃162013301179835643598576559　　3,、、,。3　/(g·cm-3)30～380℃2.512.49(×10-7/℃)88～9490(nD)1.521.50/(N·m-1)220×10-3380×10-30.880.91/℃[104.0dPa·S]10341179/℃[107.6dPa·S]730835/℃[1013.0dPa·S]546589/℃[1014.5dPa·S]4985592　2.1　,,。,、,、,、,,。,、。,,,,,2[3]。2.2　,,,10332　22　　　　　　　,,　,:　　　　　,-,1。103.7～104.2dPa·S、,1172～1240℃;104.4～106.3dPa·S,950～1160℃。,,,,200～250℃。1320～1380℃,。,90%。,Al2O3、MgO,,、。,、。30μm,,0.15μm/20mm。、、,。2.2.1　,。Vα,3,V·sinα,[4],,,,、,,i。、,[5]。,1#n#,,,。,,。,,V·sinα。α。,,,,,,V·sinα,(n#)。,,X(t/d)=W·δ·V·ρ,,W;δ;V;ρ。ρ,,,,W1δ1V1≈W2δ2V2…≈WnδnVn。,,,1,12,,。δ,V,[4]。,,i。,i1=V2/V1,i2=V3/104　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　201011V2,…,in-1=Vn/Vn-1。,i,,i(i1=i2=…in-1),。2.2.2　,。,,。,“”,“”,。,,。。。,,200～400mm。,。,。,,。,。,。,,,1℃,3.5%。,。。,,,。,。,。,,。2.2.3　,,,。,。,,,,,,,。,3～9,,15～90°,145°,,15～30°4[6]。(下转第118页)10532　22　　　　　　　,,　,:　　　　　300mm×300mm,0.1mm,60mm。c.,K2.58W/m2K,K,。[1]　,.“”[J].,2007(2):61-63.[2]　.[J].,2007(6):10-13.[3]　,,,.[J].,2001,35(1):99-101.[4]　CollinsRE,SimkoTM.CurrentStatusoftheScienceandTechnologyofVacuumGlazing[J].SolarEnergy,1998,62(2):189-213.[5]　·S.()[M].:,1979.[6]　,,.[J].,2002,23(4):90-95.[7]　.[D].:,2005.[8]　,,.[J].2007,182.[9]　,.21“”[M].:,2002.[10]　ZhangQC.TheMeasurementandCalculationofRadioactiveHeatTransferBetweenUncoatedandDopedTinOxideCoatedGlassSurfaces[J].IntJHeatMassTransfer,1997,40(1):61-71.[11]　HolmR.ElectricalContacts,TheoryandApplication[M].Berlin:Springer-Verlag,1979.[12]　WilsonCF,SimkoTM,CollinsRE.HeatConductionThroughtheSupportPillarsinVacuumGlazing[J].SolarEnergy,1998,63(6):393-406.[13]　CollinsRE,Fischer-CrippsAC.DesignofSupportPillarArraysinFlatEvacuatedWindows[J].SolarEnergy,1991,44:544-563.(上接第105页)3　　,,1mm,。,i,、,,。[1]　[P]...CN200810147442.3.[2]　　,,,.[M].:,2009.[3]　,.[M].:,2009.[4]　,,.[J].,2009,30(2):47-50,72.[5]　,　,,.1.1mm[J].,2004(2):23-28.[6]　[P]...CN200510118547.2.118　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　　201011