高岭土动态膜的制备卓琳云

整理文档很辛苦,赏杯茶钱您下走!

免费阅读已结束,点击下载阅读编辑剩下 ...

阅读已结束,您可以下载文档离线阅读编辑

资源描述

:1007-8924(2006)03-0037-04高岭土动态膜的制备卓琳云,李 俊,陈季华,李 方(,200051) :以陶瓷膜管为基质,研究了高岭土动态膜的制备过程.实验以高岭土为动态膜预涂材料,采用错流操作对膜管进行涂膜,通过记录和分析涂膜过程中的渗透液通量和测定在此过程中涂上的高岭土的量随时间的变化,研究了高岭土粒径、涂膜液浓度、跨膜压力、错流速度和涂膜时间对涂膜效果及清水通量的影响,对涂膜过程有了较好的认识,并得出最佳涂膜条件为:涂膜液质量浓度0.3g/L、跨膜压力0.2MPa、错流速度0.5m/s及涂膜时间10min.:高岭土;陶瓷膜;动态膜;错流微滤:X703  :A  (Dynamicmembrane),(Secondmembrane)[1].,..,(、、、、MnO2),.1965OakRidgeZrOCl2.,,,,,,[2].,Anderson[3]KMnO4MnO2.[4]、Yoshiski.Kiso[5].Johari[6].,,、,.,,,.6000,,.1 实验材料及方法1.1 ,α-Al2O3,9mm,13mm,38cm,2μm.,1250、4000、6000.表1 高岭土目数与粒径的换算Tabel1 Conversionofkaolinmeshandparticlesize/1250200040006000/μm1063.122.09:2004-09-17;:2004-12-06:(012312032):(1980-),,,,.26 3     Vol.26 No.320066MEMBRANESCIENCEANDTECHNOLOGYJun.2006DOI:10.16159/j.cnki.issn1007-8924.2006.03.0081.2 1.,,,,,,,,..,.1、2.;3.;4.;5、6.;7.;8、9、10.;11.1 Fig.1 Flowdiagramofprocess.20,..,,.,.,.,.,.,,,.,,,.,.NaOH,pH13~14,1h,pH1~20.5~1h..1.3 ,.,.J=ΔVπdl·Δt,J,d,l.,,10s,ΔtΔV.,.ΔVJ20℃..SS..2 结果与讨论2.1 ,0.7g/L、0.5m/s、0.2MPa,3.(2),,,JpRtJ=Δp/ηRt,.,[7].,,.,(),(6000).2 Fig.2 Relationshipbetweenfluxandtimeatvariouskaolinparticlesizes ·38   ·     26 2.2 0.5,1.0,1.5、2m/s,0.2MPa,0.3g/L,10min.,1,1.5,2m/s,.0.5m/s,.0.5m/s.2.3 ,.0.5m/s,0.3g/L,0.1,0.2,0.3,0.4MPa.(3),,.0.2MPa0.3MPa,,,0.2MPa.3 Fig.3 Membranefluxwithrespecttotimeandatvariouspressure2.4 0.5m/s、0.2MPa,(0.1,0.3,0.5,0.7g/L),.,,,,,.4,0.3g/L0.1g/L,,,,.,,,.,,0.3g/L.4 Fig.4 Membranefluxwithrespecttotimeandatvariouskaolinconcentrations2.5 2.5.1 (0.5m/s),(0.3g/L),,(5).,.,(0.3,0.4MPa),,,10~20min.(0.1,0.2MPa),.5 Fig.5 Kaolinweightwithrespecttotimeandatvariouspressure2.5.2 (0.5m/s),(0.2MPa),,(6).,,.0.5,0.7g/L,,1h.0.1,0.3g/L,1h.5、6,,3、4,, 3:·39   · 6 Fig.6 Kaolinweightwithrespecttotimeandatvariouskaolinconcentrations20min,.3 结论2μm,,,,:1),,,,6000.  2),0.5m/s,0.2MPa0.3g/L.3)、,10~20min,.[1] ,,,.[J].,2003,19:29-31.[2], ,.[J].,2003,23(3):49-53.[3]MuhammadHA,AndersonGK.Crossflowmicrofiltra-tionwithdynamicmembrane[J].WatResSci,1997,31(8):1969-1979.[4],.-[J].,2002,23(6):51-56.[5]YoshiakiKiso.Wastewatertreatmentperformanceofafil-trationbio-reactorequippedwithameshasafiltermate-rial[J].WatRes,2000,34(17):4143-4150.[6]MegatJMMN,FakhrulRA.Performanceofflexiblemembraneusingdynamincmembraneintreatingdomesticwastewater[J].Des,2002,147:263-268.[7], ,,.[J].,2001,21(6):560-563.PreparationofdynamicallyformedmembranefromkaolinZHUOLinyun,LIJun,CHENJihua,LIFang(InstituteofEnvironmentScienceandTechnology,DonghuaUniversity,Shanghai200051,China)Abstract:ThePreparationofdynamicallyformedmembraneonthetopofceramicsupportwasinvestigatedwithcrossflowoperation.Thefluxofthemembrane,andtheamountofkaolindepositedontheinnerwallofthece-ramictubeweremeasuredduringtheexperiment.Theeffectsareparticlesizes,concentrationofkaolin,trans-membranepressure,crossflowvelocityandmembrane-formingtimewereinrestigated.6000meshkaolinwasusedastheexperimentmaterial.Theresultsshowthatthebestmembrane-formingconditionwas:concentra-tionofkaolin0.3g/L,transmembranepressure0.2MPa,crossflowvelocity0.5m/s,membrane-formingwere10minitues.Keywords:kaolin;dynamicmembrane;ceramicmembrane;crossflowmicrofiltration ·40   ·     26 

1 / 4
下载文档,编辑使用

©2015-2020 m.777doc.com 三七文档.

备案号:鲁ICP备2024069028号-1 客服联系 QQ:2149211541

×
保存成功