搜索
ISO8249:2018焊接—奥氏体和双相铁素体奥氏体铬镍不锈钢焊接金属中铁素体含量（FN）的测定（中文翻译版）目录页前言......................................................................................................................................iv简介.......................................................................................................................................v1范围....................................................................................................................................12规范性引用文件................................................................................................................13术语和定义........................................................................................................................14原则....................................................................................................................................15校准....................................................................................................................................25.1涂层厚度标准.................................................................................................................25.2磁铁.................................................................................................................................25.3仪器.................................................................................................................................25.4校准曲线.........................................................................................................................36覆盖电极试验垫的标准方法............................................................................................56.1焊接金属试样的尺寸.....................................................................................................56.2熔敷金属试样.................................................................................................................56.3测量.................................................................................................................................66.3.1表面处理......................................................................................................................66.3.2单独测量......................................................................................................................66.3.3报告..............................................................................................................................77其他工艺的试验垫和生产焊缝的标准方法....................................................................77.1其他焊接金属试验垫的标准方法.................................................................................77.2生产焊缝.........................................................................................................................78其他方法............................................................................................................................78.1方法.................................................................................................................................78.2保持校准.........................................................................................................................89奥氏体不锈钢焊接金属中δ铁素体的二级标准制备程序............................................8附录A（资料性附录）带材包层制造二级标准...............................................................9附录B（资料性附录）离心冷铸二级标准的制造..........................................................19参考文献..............................................................................................................................27前言ISO（国际标准化组织）是一个由国家标准机构（ISO成员机构）组成的世界性联合会。编制国际标准的工作通常是通过ISO技术委员会进行的。对已设立技术委员会的主题感兴趣的每个成员机构都有权派代表参加该委员会。国际组织，政府和非政府组织，与国际标准化组织联络，也参与这项工作。ISO与国际电工委员会（IEC）在电工技术标准化的所有问题上密切合作。ISO/IEC指令第1部分描述了用于编制本文件和进一步维护本文件的程序。特别是，应注意不同类型的ISO文件所需的不同批准标准。本文件根据ISO/IEC指令第2部分（见）的编辑规则起草。请注意，本文件的某些要素可能是专利权的主体。ISO不负责识别任何或所有此类专利权。在编写本文件期间确定的任何专利权的详细情况将在介绍和/或收到的专利声明的ISO清单中列出（见）。本文件中使用的任何商号均为方便用户而提供的信息，不构成背书。关于标准的自愿性、与合格评定有关的ISO特定术语和表达的含义，以及关于ISO在技术性贸易壁垒（TBT）中遵守世界贸易组织（WTO）原则的信息，请参见。本文件由国际焊接学会第二委员会编写。与本文件任何方面相关的任何反馈、问题或官方解释请求应通过您的国家标准机构提交给IIW。这些机构的完整清单可以在上找到。第三版取消并取代第二版（ISO8249:2000），该版本已进行了技术修订。与上一版相比，主要变化如下：—对表2（原表1）进行了更正；—对第9条（原第8条）和整个文件进行了细微的编辑性修改。介绍目前，对于测量焊缝金属中的铁素体含量最好的实验方法，无论是破坏性的还是非破坏性的，还没有统一的意见。这种情况导致了国际上“铁素体数”或FN概念的发展和使用。铁素体含量是用标准化程序确定的焊缝金属铁素体含量的描述。本文件规定了这些程序。焊缝金属的铁素体含量被认为与铁素体含量的百分比近似相等，特别是在FN值较低的情况下。最近的信息表明，FN可以高估较高FN时的铁素体体积百分率，高估系数的顺序为1,3到1,5，这在一定程度上取决于合金的实际成分。尽管有其他方法可用于确定铁素体含量，但本文件中规定的标准化测量程序是基于评估从具有规定强度和尺寸的磁铁中提取焊接金属样品所需的撕裂力。撕裂力与FN之间的关系是通过在磁性基底上使用由指定厚度的非磁性涂层组成的一级标准得到的。每个非磁性涂层厚度都指定了一个FN值。用这种方法测定的铁素体含量是任意的，不一定是真实的或绝对的铁素体含量。认识到这一事实，在引用由该方法确定的铁素体含量时，使用术语“铁素体含量”（FN）而不是“铁素体百分比”。为了有助于传达这样一个信息，即已经使用了这种标准化的校准程序，“铁素体数”和“FN”这两个术语被大写为专有名词。焊接—奥氏体和双相铁素体奥氏体铬镍不锈钢焊接金属中铁素体含量（FN）的测定1、范围本文件规定了以下方法和装置：—通过焊接金属样品和标准永磁体之间的吸引力，测量主要为奥氏体和双铁素体奥氏体不锈钢1）焊接金属中δ铁素体含量，表示为铁素体含量（FN）；1）术语“奥氏体-铁素体（双相）不锈钢”有时用于代替“双相铁素体-奥氏体不锈钢”。—手工金属电弧覆盖电极标准焊盘的制备和测量。对于生产焊缝的铁素体测量和其他工艺（如钨极气体保护焊、气体保护焊和埋弧焊）的焊缝金属，也推荐使用一般方法（在这种情况下，应确定焊盘的生产方式）；—校准其他仪器来测量FN。本文件中规定的方法适用于焊态焊接金属和热处理后导致铁素体完全或部分转变为任何非磁性相的焊接金属。奥氏体