海上风机基础钢结构防腐蚀设计

乐治济，林毅峰。、、。。。doi10.7640/zggwjs201304005AnticorrosiveDesignforSteelStructuredFoundationforOffshoreWindTurbinesYUEZhi-jiLINYi-fengShanghaiInvestigationDesign&ResearchInstituteShanghai200434ChinaAbstractThepapersummarizesthecharacteristicsofcorrosionoffoundationsforoffshorewindturbinesandtheanticorro－sivemeasuresincommonuseforoffshorewindturbinefoundations.Thetechnologyofanticorrosioncoatinginatmosphericzonewherehighweathersustainabilityisrequiredandthetechnologyofanticorrosioncoatingandwrappinginthesplashandtidalzoneswherehighcorrosionresistanceisrequiredareanalyzedandcompared.Itisthenrecommendedthatacorrosionprotectiondesignforanoffshorewindturbinefoundationshouldtakeintoconsiderationthefulllifecycleofthefoundationinitswholeconstructionandoperationaldurationandrelativedesignconsiderationsareputforwardforthereferenceforselec－tionofcorrosionprotectiondesignsofoffshorewindturbinefields.KeywordsAug.“—”“”“”—。0、、、。、、5MW100MW100MW。2015500kW。。25a28a。。。1、、、。。。。。5、、、。0.05~0.15mm/a[1]、、0.3~0.5mm/a[2]0.1~0.2mm/a[2]。。。。、。。2、、。。。。。。。。1。。。。。。。“”[2]。。315a、[3-6]。、、[3-6]。、。10a。、1、、、、、、、、、、19··、、、、。VOC、。、VOC、。。。3~4。。4、、、。。。。。。。4.1重防腐涂料防腐、、、、[7-10]。、、、、。、、、25t。。30a。。、、、。。。。。100%[11]、、。20。。。、25a。。4.2包覆防腐、、、[212-15]。、、、、、。、。。30a。PTCDenso[15]。PTC、、、。Denso、、20··2008、、、[16]。、。、、、。2.5mm58.1a。、、、、、、。15a17a。。。、。40090/10。1~2μm/a[17]。。。。。、。。。、、、。。[18]。2。。100%。。5a10~15a。。。。。5、。。12/·m-280801001002000240220012021··。2、、。3。。。。。4。、、、。。5。“”。。。、。。6、。。。。7、。6。、。。。[1].[M].19994-12.[2].[M].201110-100.[3].[M].2007107-208.[4].[J].20081037-39.[5].[J].2011658-66.[6].[J].2012735-41.[7].[J].20051233-35.[8].[J].2005339-43.[9].[J].2006351-54.[10].[J].2011437-41.[11].100%[J].2005629-32.[12].[M].1993213-216.[13].[J].198122-14.[14].[J]..201210833-836.[15].[J].2004422-36.[16].[J].2012270-72.[17].[J].20122100-102.[18].[J].1993227-32.22··