玻璃中气体的存在形式及气泡产生的原因

目录摘要...................................................................................................1ABSTRACT.....................................................................................................1绪论...................................................................................................21.1玻璃的历史及应用...................................................................31.2玻璃的简单分类.....................................................................41.3玻璃按主要成分的分类.........................................................51.4玻璃按性能的分类.................................................................61.5玻璃的生产工艺.....................................................................6第二章玻璃中存在的气泡类型及分类................................82.1一次气泡.................................................................................82.1.1消除一次气泡的理论依据..........................................................82.2二次气泡.................................................................................92.2.1二次气泡产生的机理................................................................92.3外界空气气泡.........................................................................102.4耐火材料引起的气泡.............................................................102.5杂质引起的气泡.....................................................................102.6玻璃中气体的存在形式及在玻璃熔体中的溶解度.............102.6.1碳酸盐分解产物和燃烧产物CO2.......................................102.6.2硫酸盐分解产物和燃烧产物S02.........................................112.6.3O2.....................................................................................................112.6.4H2O..................................................................................................112.6.5H2....................................................................................................122.6.6N2....................................................................................................122.7气泡产生的原因分析...........................................................132.7.1泡源位置的判断...........................................................................132.7.2依据气泡在玻璃板的分布判断...............................................132.7.3依据气泡的大小判断..................................................................142.7.4依据形成原因的判断..................................................................142.8熔窑部产生的气泡缺陷分.....................................................142.9锡槽部的气泡产生原因.........................................................162.10二次气泡的产生原因.........................................................172.11由杂质产生的气泡...............................................................182.12玻璃液与耐火材料接触所引起的气泡...............................19第三章气泡的解决措施..........................................................203.1一次气泡.................................................................................213.2二次气泡.................................................................................213.3外界空气气泡.........................................................................223.4耐火材料引起的气泡.............................................................223.5杂质引起的气泡.....................................................................233.6减少微气泡拟采取的主要措施.............................................23第四章结论...............................................................................24致谢........................................................................................25参考文献........................................................................................271摘要气泡是玻璃生产的主要缺陷之一，气泡不仅影响玻璃的透明性、机械强度，在玻璃深加工领域，气泡是鉴定原片质量的关键指标。通过对玻璃生产中气泡类型的研究，探讨玻璃中气体的存在形式及气泡产生的原因，并结合生产实际来研究解决气泡问题的办法，达到提高玻璃生产质量的目的。关键词玻璃气泡产生原因解决措施AbstractBubbleisoneofthemainshortcomingsforglassproduction,thebubblenotonlyaffectthetransparencyoftheglass,mechanicalstrength,theglassdeep-processingareas,identificationoftheoriginalfilmBubbleisthequalityofkeyindicators.Throughthestudyonthetypeofbubbleintheglassproductionduringtheformationofgasbubblesandthecause,combinedwiththeactualproductionofglasses，westudyandsolvethebubblesproblems,toimprovethequalityofglassproductionpurposes.Keyword：glass;AirbubbleProducecause;Resolvemeasurement2绪论实际生产中，产生气泡的原因很多，以采取相应的措施加以解决。一般来说，浮法玻璃生产实践中气泡主要产生于玻璃的熔制过程中，其次在锡槽成形过程中也有可能产生气泡［1］。将气泡按其产生的来源分类会有助于寻找气泡产生的原因。第一类是所谓澄清气泡，是在初熔及澄清之后残余在玻璃中的气泡;第二类是玻璃熔体中大体已不存在气泡以后，在某一时间又从玻璃中析出所分解的气体而形成的气泡，称为再生气泡(重沸气泡);第三类是气泡中有些夹杂的气态、态或固态异物。它们是空气泡、工作气泡、铁质气泡、污染气泡等。分清气泡是属于三类中的那一类就可推测气泡缺陷是在那个区域产生的［2］，这对采取什么样的消除缺陷措施致关重要。气泡数、气泡大小及其分配情况、气泡中和气泡附近的物质在显微镜下的观察结果、玻璃中气泡的位置、气泡中的气体分析等都是诊断气泡缺陷的重要特征参数。玻璃气泡是玻璃中的气体以可见形态存在的形式，是气态夹杂物，不仅影响玻璃制品的外观质量，更重要的是影响玻璃的透明性和机械强度。存在于玻璃液中的气体主要有三种状态，既可见气泡、溶解的气体、化学结合的气体。在浮法玻璃生产过程中，原料种类、炉气性质和压力、熔制温度等不同，在玻璃中的气体种类和数量也不同，常见的气体有O2,H2,H,O,CO,CO2,SO2,N2,Ar等。3第一章玻璃的发展及分类1.1玻璃的历史及应用玻璃最初由火山喷出的酸性岩凝固而得。约公元前3700年前，古埃及人已制出玻璃装饰品和简单玻璃器皿，当时只有有色玻璃，约公元前1000年前，中国制造出无色玻璃。公元12世纪，出现了商品玻璃，并开始成为工业材料。18世纪，为适应研制望远镜的需要，制出光学玻璃。1873年，比利时首先制出平板玻璃。1906年，美国制出平板玻璃引上机。此后，随着玻璃生产的工业化和规模化，各种用途和各种性能的玻璃相继问世。现代，玻璃已成为日常生活、生产和科学技术领域的重要材料。3000多年前，一艘欧洲腓尼基人的商船，满载着晶体矿物“天然苏打”，航行在地中海沿岸的贝鲁斯河上。由于海水落潮，商船搁浅了。于是，船员们纷纷登上沙滩。有的船员还抬来