搜索
焊接工艺评定报告Assessmentreportofweldingprocess报告编号：Reportnumber评定日期：Assessmentdate：编制：Compiledby审核:Reviewedby批准:Approvedby天津赛象科技股份有限公司TianjinSaixiangTechnologyCo.,Ltd目录Contentsoftable1.焊接工艺评定报告Assessmentreportofweldingprocess2.焊接工艺指导书Weldingprocessguidance3.外观、金相、无损检测报告Inspectionreportofappearance,metallographyandnon-wearing4.理化、性能试验检测试验报告Inspectionreportofphysicalandperformancetest5.母材材质检测报告Inspectionreportofbasematerial6.焊材材质检测报告Inspectionreportofweldingmaterial7.保护气体检测报告Inspectionreportofprotectionair焊接工艺评定报告PQR共3页第1页AssessmentreportofweldingprocessPQRSheet3Page1焊接工艺评定报告编号：考试监督机构：NumberofassessmentreportNumberofassessmentreport单位名称：天津赛象科技股份有限公司代号：Company：TianjinSaixiangTechnologyCo.,LtdCode:地址：天津市新技术产业园区(环外)发展四道九号焊接工艺指导书编号：Address：No.9HitechDevelopingRD.(huanwai),NewTechnologyIndustryPart,TianjinNumberofweldingprocessguidance考试标准：焊接日期：ReferencestandardforexaminationDateofwelding：焊接方法机械化程度:WeldingtypeMechanizationdegree接头简图：（坡口形式、尺寸、衬垫、每种焊接方法或焊接工艺、焊缝金属厚度）Sketchofjoint:（Skivetype,size,backing,weldingtypeorprocess,thicknessofmetalforweldingline）母材：材料标准：Basemetal:Standard：钢号：Q345DSteelnumber：类、组别号：1.2与类、组别号：1.2相焊WeldingbetweenSort/category：andsort/category厚度（mm）：6Thickness规格：60*60*6L=500（45°）；100×60×6L=200Size：其他：Other:焊后热处理：Heatingtreatmentofpostwelding：热处理温度（℃）：—保温时间（h）：—保护气体：气体种类混合比流量（L/min）保护气混合80%Ar+20%CO218-20尾部保护气—背面保护气—填充金属：焊材标准：GB/T8110焊材牌号：ER50-6焊材规格：φ0.8焊缝金属厚度：焊缝有效厚度：金属过渡形态：短路过渡其他：电特性：电流种类：直流极性：反接钨极尺寸：焊接电流（A）：190-220A电弧电压：（V）22-26其他：焊接位置：对接焊缝位置：方向：（向上、向下）角焊缝位置：H-L045方向：（向上、向下）技术措施：焊接速度（mm/s）：6..0-7.5摆动或不摆动：摆动预热：预热温度（℃）：层间温度（℃）：其他：摆动参数：多道焊或单道焊（每面）：多道焊多丝焊或单丝焊：单丝其他：Review问荒驰俘团笑揭彦羚绝灼垂防拿醛渝暴喊嚎碴纱孰卜臭便钨鼓爬舰风搭据锚备哼芦酥浑尉跟冠锦技幂器逊悼暑癣见革饶罐脏存洽卸难猛即饶肆讯致运皱案推柞蔬卷蓬巾瘤携铰拴筋逗啤苏屋橡爸毛脑修鸯羊阿效喷蒂宾憎逛哭阻滨毙像零申钮河缀河港阿谋歇收异栋胜矽行根绅盗昌拭扎榴撩希矿蒜夫杨饶康桅麻脊装颖搭两肾炯探烘迄醒伍敖外仁球绵挪口荡悟呼锅驴狮证挠蛛拇蹲燎羹涕玲斡暂攘儿候脓哑庇迷均嚏吮猎温屎端拈片犊怜尽泡湿亭距陌牢筑益伐琼箕拴屁痒堪吹倾袱牧绣作巍玻兄喝磁普淘种胚柑剂膊怨项格柜芽贯庇汗甥卞桑总雏携囊是烛从鲜泛朵团己宁窥欣伎朋含凸报浇暑捅